ASTM A240 A480 EN1.4016 430 Stainless Steel Sheet Width 2000mm Above Product Description 430 stainless steel plate has all the characteristics of 430 stainless steel.It is a general-purpose steel with good corrosion resistance. Its thermal conductivity is better than that of austenite, and its thermal expansion coefficient is smaller than that of austenite. It is heat-resistant and fatigue resistant.It is added with stabilizing and has good mechanical properties at the weld. Product Diaplay
| Chemicai Composition(WT%) | ||||||||
| Grade | (C) | (Si) | (Mn) | (Cr) | (N) | (Ni) | (P) | (S) |
| 430 | ≤0.12 | ≤1.0 | ≤1.0 | 16.0~18.0 | ≤1.0 | ≤0.6 | ≤0.040 | ≤0.030 |
| sical Property | ||||||||
| yield strength(mpa) | tensile strength(mpa) | extend(%) | ||||||
| ≥205 | ≥450 | ≥22 | ||||||
Application | ||||||||
| Building decoration, fuel burner parts, household appliances, household appliances parts | ||||||||
Manufacturing Process of stainless steel sheet
Raw materials are sending to hot rolling units for rolling into different sizes.
→Hot rolled material is annealing in cold rolled annealing furnace and pickling in acid.
→All mill rolls are grinded on precision grinding machine with proper chamfering after first shift .
→All sheets are pickled in different tanks and dried on brush roll machine before dispatched.
→These sheets are again annealing and are sent to straighten machine for straightening.
→Inspections are done at various stages. Keep proper control overall internal process via rolling.Features And Processing Technology1D - the surface has discontinuous granular shape, also known as fog surface.Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.2D - slightly shiny silver white.Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.2B - silver white and better gloss and flatness than 2D surface.Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling+ quenching and tempering rolling.BA - exnt surface gloss and high reflectivity, like mirror surface.Processing technology: hot rolling + annealing shot peening and pickling + cold rolling + annealing and pickling+ surface polishing + tempering and rolling.NO.3 - has good gloss and rough surface.Processing technology: polishing, tempering and rolling of 2D products or 2B with 100 ~ 120 grinding materials (JIS R6002).NO.4 - has good gloss and fine the surface.Processing technology: polishing, tempering and rolling of 2D products or 2B with 150 ~ 180 grinding materials (JIS R6002).HL - silver gray with hair stripes.Processing technology: the 2D or 2B products are polished with abrasive materials ofappropriate particle size to make the surface appear continuous grinding pan>