Characteristic:High strength and cohesive force, good abrasion resistance
Â
Application: Double density sole system for common safety shoes and one-step forming casual shoes, outsole
Â
Typical properties of PU pan>
Â
| Name of products | Appearance | Viscoscity (mPa·s/40℃) | Density (g·cm-³/40℃) |  Package (kg) |
| Â A-6170 | Â liqud | Â 1000-1400 | Â 1.01-1.02 | Â 18 |
| Â B-8280 | Â Yellowish Transparent liquid or waxy | 600-1000 | Â 1.08-1.2 | Â 20 |
Â
Materials preheat
Â
A-6170: preheated at 50-60℃ for 6-8℃ hours
B-8280: preheated at 50-60℃ for 8-12 hours
Â
Typical processing parameters & Reaction parameter
Â
| Items | A/B Materials Temperatures(℃) | Mix ratio A+C/B (By weight)  | Cream time (s) |  End of Rise Time (s) | ||
| Â Parameter | Â 40-45/40-45 | Â sole | mid-sole | sole | mid-sole | Â 40-50Â |
| 100/69-71 | 100/77-79 | 6-8 | 6-7 | |||
| Items | Free Rise Foam Density (g/cm³) | Mold Temperature (℃) | Demold Time (min) | |
| parameter | sole | mid-sole | 45-55 | 3-5 |
| 0.60-1.0 | 0.23-0.27 | |||
Â
The adding content of C-2 should be 300g±10g/18kg
The adding content of water and hardener should be changed according to the reality
Â
Sole:           H2O 0-30g/18kg     Hardener 0-400g/18kg
Mid-sole:        H2O 50-55g/18kg    Hardener 0-600g/18kg
Â
sical properties
Â
| Items | Molded Density (g/cm³)  | Hardness (Shore A)  |  Tensile strength (Mpa)  |   Elongation (%)   | ||||
 sical properties  |  sole | mid-sole |  sole | mid-sole |  sole | mid-sole | sole | mid-sole |
| 0.9-1.1 | 0.45-0.55 | 62-72 | 45-55 | 8.0-11.0 | 3.9-7.9 | 550-750 | 520-690 | |
| Items | Tear strength (kN/m) | Flexing resistance | DIN abrasion (mm³) | Peel strength between sole and mid-sole (kN/m) | ||
| sical properties | sole | mid-sole | 100000 times no crack | sole | mid-sole | ≥3.5 |
| 25-40 | 16-27 | 60-100 | ---- | |||
Â
Demold time may be prolonged with the increse of sole thickness
These sical data are acquired by testing a sample of 6mm thick
Data listed above are just for reference.The data are subjected to practical production.If other requests for sical properties,please us.Â