Name of product: XC-2216S, XC-6110
Characteristic: Good handle, smooth surface, low density and low hardness, good dimension stability
Application: Insole, Midsole
Appearance: XC-2216S: Liquid, XC-6110: Yellowish transparent liquid or waxy
Package: 20kgs or 18 kgs
Material preheat: XC-2216S: Preheated at 50-60 ℃ for 8-10 hours
XC- 6110: Preheated at 50-60 ℃ for 8-10 hours
Typical processing parameters & Reaction parameter
| Item | A/B material temperature(℃) | A/B material mix ratio | Cream time(s) | End of rise time(s) | Free rise foam density(g/cm³) | Mold temperature(℃) | Demold time(min) |
| Parameter | 40-45/38-42 | 100-69-71 | 4-6 | 35-50 | 0.14-0.21 | 45-55 | 3-5 |
The adding content of C-2 should be 300±10g/18kg
The adding content of water should be 0-90g/18kg according to the reality
The adding content of hardener should be changed according to the reality
sical properties
| Item | Demold density(g/cm³) | Hardness (Shore C) | Tensile strength(Mpa) | Elongation(%) | Angel tear strength(kN/m) |
| sical properties | 0.28-0.4 | 28-50 | 1.5-2.8 | 380-450 | 9-15 |
Demold time may be prolonged with the increase of sole thickness
These sical data are acquired by testing a sample of 6mm thick
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for sical properties, please us.