Products description
Characteristic:Good handle, low density and good dimension stability
Application:Outsole and slippers
Typical properties of PU > Name of products Viscoscity (mPa·s/40℃) Density (g·cm-³/40℃) Package (kg) Name of products Viscoscity (mPa·s/40℃) Density (g·cm-³/40℃) Package (kg) A-2260: preheated at 50-60℃ for 6-8 hours B-8580: preheated at 50-60℃ for 8-10 hours Typical processing parameters & Reaction parameter Mix ratio A+C+70H2O/B (By weight) Cream time (s) End of Rise Time (s) Free Rise Foam Density (g/cm³) Mold Temperature Demold Time (℃) 4-5 The adding content of C-2 should be 270g±10g/18kg The adding content of water should be 0-70g/18kg according to the reality The adding content of hardener should be changed according to the reality sical properties Molded Density (g/cm³) Hardness (Shore A) Tensile strength (Mpa) Elongation (%) Tear Strength (kN/m) Ross Flexing (room temperature) (50000times) sical properties Demold time may be prolonged with the increse of sole thickness These sical data are acquired by testing a sample of 6mm thick Data listed above are just for reference.The data are subjected to practical production.If other requests for sical properties,please us. Appearance A-2260 Cream white liqud 800-1200 1.01-1.02 18 B-8580 Yellowish Transparent liquid or waxy 600-800 1.08-1.2
Materials preheatAppearance A-2260 Cream white liqud 800-1200 1.01-1.02 18 B-8580 Yellowish Transparent liquid or waxy 600-800 1.08-1.2 20 Items A/B Materials Temperatures(℃) Parameter 40-45/38-42 100/98.5-100.5 6-8 40-50 0.15-0.25 45-55 Items 0.30-0.45 43-58 2.9-5.0 250-400 10-26 No crack 
Signup today to claim your Discount. Get Started before it's too late!