Perforated steel sheet for making of pipes or tubes: 1mm thickness, 4mm hole diameter, 7mm distance between holes, triaged 60 degree, 20mm free all side.Perforated black steel Q235 applied for processing of tubing: 1.5mm thickness, 4mm hole diameter, 7mm distance between holes, triaged 60 degree,20mm free all side
This type of perforated tubing is made of high quality low carbon plain steel sheet after being perforated on the digital control perforated machines. It you don't see what you are looking for, we can custom punch many patterns.
| GAUGE | HOLES | CENTERS | OPEN AREA % |
| 26 | .020" | .043" | 20% |
| 26 | .027" | .050" STRAIGHT | 23% |
| 22 | 1/32" | 1/16" | 22% |
| 22-18 | 3/64" | 3/32" | 23% |
| 24 | .050" | .066" STRAIGHT | 45% |
| 22-18 | 1/16" | 3/32" | 45% |
| 16 | 1/16" | 7/64" | 30% |
| 20-16 | 1/16" | 1/8" | 23% |
| 20-14 | 5/64" | 1/8" | 36% |
| 20-14 | 3/32" | 5/32" | 33% |
| 24 | 3/32" | 3/16" | 23% |
| 18 | .117" | 5/32" | 51% |
| 22,18-14,11 | 1/8" | 3/16" | 40% |
| 12 | 1/8" | 7/32" | 29% |
| 18 | 9/64" | 3/16" | 51% |
| 20-16 | 5/32" | 3/16" | 63% |
| 20,10 | 5/32" | 1/4" | 36% |
| 22,18,16 | 3/16" | 7/32" | 67% |
| 24-14 | 3/16" | 1/4" | 51% |
| 18-3/16"PL | 3/16" | 5/16" | 33% |
| 22 | 1/4" | HEX | 79% |
| 22-16 | 1/4" | 5/16" | 58% |
| 20-1/4"PL | 1/4" | 3/8" | 40% |
| 16 | 1/4" | 3/8" STRAIGHT | 35% |
| 18 | 1/4" | 1/2"STRAIGHT | 23% |
| 18-14,10,3/16"1/4"PL | 5/16" | 7/16" | 50% |
| 16-1/4"PL | 3/8" | 9/16" | 40% |
| 20-14,10-1/4"PL | 1/2" | 11/16" | 48% |
| 10-1/4"PL | 5/8" | 7/8" | 46% |
| 16,11,3/16",1/4"PL | 3/4" | 1" | 51% |
| 10-1/4"PL | 1" | 1-3/8" | 48% |
| 3/16",1/4"PL | 1-1/4" | 1-5/8" | 54% |
| 10-1/4"PL | 1-1/2" | 2" | 51% |
| 10-1/4"PL | 2" | 2-1/2" | 58% |
| 10,3/16"PL | 2-1/2" | 3" | 63% |
| 10,1/4"PL | 3" | 3-1/2" | 67% |
| 10 | 3-1/2" | 4" | 70% |
| 10 | 4" | 4-1/2" | 72% |
Carbon Steel Materials Applied for Perforated Tubes Manufacturing:
Stainless Steel, unlike carbon steel, is corrosion resistant. It contains chromium which, when exposed to oxygen, creates an invisible protective film. Stainless steel types are classified into three different groups based on their ability to be hardened. Austenitic stainless steels, which can be hardened by cold working, meet a wide range of design criteria. They are essentially non-magnetic, although they may become slightly magnetic due to cold working.
Because carbon steel is susceptible to corrosion, it is typically used in either unexposed applications or protected with a coating. Coatings such as paint and powder are applied after perforating and completely protect the material. Zinc based coated metals (i.e. Galvanized, Galvannealed, etc.) on the other hand, are produced and supplied as such from the mill and may not completely protect the material where its carbon core is exposed during the perforating process.
Commonly Perforated Carbon Steel TypesCommercial Steel (HR, CR, GALV) A low cost steel that has good drawing, forming, and welding qualities, moderate strength, but is subject to strains, fluting, and breaks due to aging. To reduce the affects caused by aging, Drawing Steel is recommended.