Degree of whiteness 96 min
water / plaster ratio 100- 125 %
Initial setting time 6:12 minutes
final setting time 15 - 28 %
fluidity 250 - 320 %
water absorption > 32 %
bending strength > 35 Kg /Cm2
compressive strength > 90 Kg / cm2
fineness, retained on sieve 0.15 mm (100 mesh) < 4 %