Cover | PE film, Sand, Minnerals etc. |
Wide | 1Meter |
Length | 7.5- 10 meters |
Thickness | 3.0mm 4.0mm |
Plastomer APP Modified Bitumen Torch Applied Waterproofing Membrane is a kind of torch on application membrane manufactured by using advanced Germany technology and direct mixing process. Select APP (Atactic Polypropylene) or APAO, APO (polyolefin polymer) modified aslt as dipping material, reinforced with polyester felt, glass fiber felt and glass fiber reinforced polyester felt, surface covered with fine sand, mineral grain (sheet) material, PE film, refined by advanced technology plastic modified bitumen waterproof membrane. It is widely used in the basement and rooftop waterproofing works with advanced performance.
Basic Specification | ||||
Reinforced Layer | Thickness (mm) | Width (mm) | Surface | Torching side |
Polyester felt (PY) | 3 / 4 | 1000 | Polyethylene (PE) Fine Sand (S) Mineral aggregate (M) | Polyethylene (PE) |
Fiberglass felt (G) | 3 / 4 |
Product Feature
1. Good elasticity, high tensile strength and elongation, good high temperature flexibility, good wear resistance.
2. Exnt water impermeability and temperature adaptability. APP is suitable for building waterproofing in lower temperature environments.
3. Good corrosion resistance and aging resistance, anti-puncture resistance, mildew resistance, impact resistance, pressure resistance, long service life.
4. Easy to operate and maintain, and ensure the construction quality.
5. Specially designed for hot aslt or heat welding(with burn-off polyethylene)applications. heat welding lap joints are durable, reliable, and tight.
 Application Scope
1. Suitable for waterproofing and moisture proofing of roofs, basements and industrial cold storage as well as civil building structures.
2. Waterproofing for water conservancy projects, swimming pools, bridge decks, subways, tunnels, sewage treatment plants, landfills, etc.
3. It can also be used for anti-corrosion and various moisture-proof interior packaging materials of underground pipepan>
Transportation & Storage
1. There should be a dedicated warehouse stacking and the warehouse must be ventilated to avoid light exposure, non-fire sources, and fire prevention.
2. When stacking in temporary warehouses on the construction site, coverings must be covered to avoid sun and rain. When transporting, the membranes should be stacked tightly and the membranes cannot be stacked on each other to prevent the sheet from tilting or lateral pressure. The storage temperature should be not higher than 50°C, the storage period is one year from the date of production, and it can still be used if it is qualified.
Working Advice
If there is any snow, water or frost on the ground of the operation, must stop construct. If it is necessary to work under negative temperature, measures should be taken to ensure that the waterproof layer after laying is not cracked or sticky. During the construction, the air needs to be squeezed by hand to avoid bulging. When handling, take it upright and place it upright. The height must not exceed two layers. Prevent tilting or lateral pressure. Do not drop it and avoid damage.
Technical Data Sheet
Technical Data Sheet | ||||||
S/N | Test items | Test Value | ||||
PY | G | |||||
1 | Soluble content | 3mm | ⥠2100 g/㡠| |||
4mm | ⥠2900 g/㡠| |||||
5mm | ⥠3500 g/㡠| |||||
2 | Heat resistance | 110â,  â¤Â 2mm No flow, no dripping | ||||
3 | Low temperature flexibility | -7â, No crack | ||||
4 | Impermeable (30min) | 0.3Mpa | 0.2Mpa | |||
5 | Tension | Maximum peak tension | â¥500N/50mm | â¥500N/50mm | ||
Results | No cracking | |||||
6 | Elongation rate | Maximum peak elongation | â¥25% | |||
Second peak elongation | - | |||||
7 | Increased quality after soaking | PE/S | â¤1.0% | |||
M | â¤2.0% | |||||
8 | Thermal aging | Rally retention rate | â¥90% | |||
Elongation retention rate | â¥80% | |||||
Low temperature flexibility | -2â | |||||
No crack | ||||||
Size change rate | â¤0.7% | - | ||||
Loss of quality | â¤1.0% | |||||
9 | Joint peel strength | â¥1.0 N/mm | ||||
Mineral pellet adhesion | â¤2.0 g | |||||
The thickness of Bitumen cover layer on the downward covered surface of the membrane | â¥1.0mm | |||||
10 | Artificial weather accelerated aging | Appearance | No sliding, flowing, dripping | |||
Rally retention rate | â¥80% | |||||
Low temperature flexibility | -2 â No crack | -10 â No crack |