Quantity(Metric Tons) | 1 - 150 | >150 |
Est. Time(days) | 14 | To be negotiated |
PP is a nonss, odorless, tasteless, creamy, high crystalmer with a density of only 0.90 --" 0.91g /cm3, "one of the lightest plastics available. It is particularly stable for water, with a water absorption rate of 0.01% and a molecular weight of about 81,150,000. Good molding performance, but due to large shrinkage rate (1%~2.5%), thick wall products are easy to sag, it is difficult to meet the requirements for some parts with high dimensional precision, and the surface of products is glossy.
Properties | Unit | Test method | Value |
Melt Flow Rate | |||
Melt flow rate(230°C/2.16KG) | g/10min | ISO 1133 | 12 |
Mechnical Properties | |||
Tensile modulus of elasticity(v=1mm/min) | Mpa | ISO 527-2 | 1550 |
Tensile yield at stress(v=50mm/min) | Mpa | ISO 527-2 | 35 |
Tensile yield at strain (v=50mm/min) | % | ISO 527-2 | 8 |
Tensile strain at break (v=50mm/min) | % | ISO 527-2 | >50 |
Charpy impact strength unnotched(+23°C) | kJ/m2 | ISO 179/1eU | 110 |
Charpy impact strength notched(+23°C) | kJ/m2 | ISO 179/1eA | 3 |
Izod Impact strength notenched(+23°C) | kJ/m2 | ISO 180/1A | 3 |
Ball indentation hardness(H 358/30) | Mpa | ISO 2039-1 | 78 |
Thermal Properties | |||
Melting point,DSC | °C | ISO 3146 | 163 |
Heat deflection temperature (0.45Mpa) | °C | ISO 75-2 | 85 |
Vicat softening temperature VST/A50(10N) | °C | ISO 306 | 154 |
Other Properties | |||
Density | g/cm3 | ISO 1183 | 0.91 |
Type | PP-H-012 | PP-H-045 | PP-H-075 | PP-H-140 | PP-H-225- | PP-H-225+ | PP-H-300- | PP-H-300+ | PP-H-425- |
MFR | 0.5-2.2 | 2-6 | 5-11 | 10-16 | 14-19 | 17-25 | 24-30 | 28-35 | 32-35 |
Stacking density | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 | 0.4-0.5 |
Ash content | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
Isotacticity | 97 | 95 | 97 | 95 | 97 | 97 | 97 | 97 | 97 |
Tensile strength | 30 | 36 | 30 | 35 | 30 | 30 | 30 | 30 | 30 |
Elongation at break | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 |
Flexural strength | 45 | 45 | 45 | 45 | 45 | 45 | 45 | 45 | 45 |
Flexural Modulus | 1300 | 1300 | 1300 | 1300 | 1100 | 1100 | 1100 | 1100 | 1100 |
IZOD Impact Strength | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 |
P045
PPMT418
PP-FR936CF
PP-ST866M
Recycled PP Injection Grade
PPIt mainly used in the household goods, food package, medicine goods, covers and toys, garden furniture etc.
25KG or 50kg/pp bag or as your requirementsÂ