Properties | Test Condition | Test Method | Unit | Typical Value |
sical | ||||
Specific Gravity | ASTM D792 | - | 1.18 | |
Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.4~0.7 | |
Melt Flow Rate | 220â/10kg | ASTM D1238 | g/10min | 60 |
Mechanical | ||||
Tensile Strength, 3.2mm | ASTM D638 | |||
@ Yield | 50mm/min | kg/cm2 | 440 | |
Tensile Elongation, 3.2mm | ASTM D638 | |||
@ Yield | 50mm/min | % | 5 | |
@ Break | 50mm/min | % | Min 20 | |
Tensile Modulus, 3.2mm | 1mm/min | ASTM D638 | kg/cm2 | 22,000 |
Flexural Strength, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 700 |
Flexural Modulus, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 26,000 |
IZOD Impact Strength, 6.4mm | ASTM D256 | |||
(Notched) | 23â | kg·cm/cm | 23 | |
-30â | kg·cm/cm | 8 | ||
IZOD Impact Strength, 3.2mm | ASTM D256 | |||
(Notched) | 23â | kg·cm/cm | 27 | |
-30â | kg·cm/cm | 8 | ||
Rockwell Hardness | R-Scale | ASTM D785 | - | 104 |
Thermal | ||||
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
(Unannealed) | 18.6kg | â | 77 | |
4.6kg | â | 84 | ||
Vicat Softening Temperature | ASTM D1525 | |||
5kg, 50â/h | â | 84 | ||
1kg, 120â/h | â | |||
Flammability | UL94 | |||
2.5mm | class | V-0 | ||
3.0mm | class | V-0 | ||
Relative Temperature Index | UL 746B | |||
Electrical | â | 80 | ||
Mechanical with Impact | â | 70 | ||
Mechanical without Impact | â | 80 |