ABS AF312C Injection Molding Grade Plastic Raw Material with Flame Retardant for Electric parts

Origin: Thailand
Supply Type: oem service
Processing Time: 7/14 days
Min Order: 30

Supplier Info.

Company Name Timbermate company limited
Membership:
Business Type: Manufacturer, Trading Company, Agent

Employees Total 5-10
Annual Revenue

Description: 1. Injection Molding ABS Grade 2. High Flame Retardant: The flame retardant performance of AF312AÂ is exnt. This material is tested based on diffrent thickness. AF312BÂ reached V0 grade at 2.5mmã€‚ 3. Widely Used: This ABS grade is the most widely used flame retardant ABS.

APPLICATIONS

Properties	Test Condition	Test Method	Unit	Typical Value
sical
Specific Gravity		ASTM D792	-	1.18
Molding Shrinkage (Flow), 3.2mm		ASTM D955	%	0.4~0.7
Melt Flow Rate	220â„ƒ/10kg	ASTM D1238	g/10min	60
Mechanical
Tensile Strength, 3.2mm		ASTM D638
@ Yield	50mm/min		kg/cm2	440
Tensile Elongation, 3.2mm		ASTM D638
@ Yield	50mm/min		%	5
@ Break	50mm/min		%	Min 20
Tensile Modulus, 3.2mm	1mm/min	ASTM D638	kg/cm2	22,000
Flexural Strength, 6.4mm	15mm/min	ASTM D790	kg/cm2	700
Flexural Modulus, 6.4mm	15mm/min	ASTM D790	kg/cm2	26,000
IZOD Impact Strength, 6.4mm		ASTM D256
(Notched)	23â„ƒ		kgÂ·cm/cm	23
	-30â„ƒ		kgÂ·cm/cm	8
IZOD Impact Strength, 3.2mm		ASTM D256
(Notched)	23â„ƒ		kgÂ·cm/cm	27
	-30â„ƒ		kgÂ·cm/cm	8
Rockwell Hardness	R-Scale	ASTM D785	-	104
Thermal
Heat Deflection Temperature, 6.4mm		ASTM D648
(Unannealed)	18.6kg		â„ƒ	77
	4.6kg		â„ƒ	84
Vicat Softening Temperature		ASTM D1525
	5kg, 50â„ƒ/h		â„ƒ	84
	1kg, 120â„ƒ/h		â„ƒ
Flammability		UL94
2.5mm			class	V-0
3.0mm			class	V-0

Relative Temperature Index		UL 746B
Electrical			â„ƒ	80
Mechanical with Impact			â„ƒ	70
Mechanical without Impact			â„ƒ	80