International code name | SK35 | SK36 | SK37 | SK38 | SK40 |
Al2O3/% | â¥48 | â¥55 | â¥65 | â¥75 | â¥80 |
Fe2O3/% | â¤2 | â¤2 | â¤2 | â¤2 | â¤2 |
Refractoriness | â¥1750 °C | â¥1770 °C | â¥1790 °C | â¥1790 °C | â¥1790 °C |
Apparent porosity | â¤22% | â¤22% | â¤23% | â¤23% | â¤21% |
Cold crushing strength | â¥39Mpa | â¥44Mpa | â¥49Mpa | â¥54Mpa | â¥65Mpa |
Refractoriness under load (0.2MPa) | â¥1420 °C | â¥1470°C | â¥1500 °C | â¥1520 °C | â¥1530 °C |
Reheating ange (1500°C 2h) % | +0.1~ -0.4*1450°C | +0.1~ -0.4 | +0.1~ -0.4 | +0.1~ -0.4 | +0.1~ -0.4 |
Features:
1.Exnt strength at ambient and elevated temperatures.2.High compressive strength.3.Very low levels of iron and other impurities.4.Lightweight and energy-efficient.5.Lower heat storage than denser refractory.6.Heats quickly and economically to operating temperature.