Item | Test conditions | Test method | Test data |
Density | ISO 1183:1987 | 1040kg/m3 | |
Water absorption | ISO 62:1999 | <0.1% | |
Melt flow rate | 200°C/5kg | ISO 1133:1997 | 3.8cm3/10min |
Process shrinkage | ISO 294-4:1997 | 1eU | |
Charpy impact strength | 1eU | ISO 179:1993 | 15kj/m2 |
Tensile modulus | 1mm/min | ISO 527-2:1993 | 3300MPa |
Elongation | 50mm/min | ISO 527-2:1993 | 3% |
Tensile strength at break | 50mm/min | ISO 527-2:1993 | 55MPa |
Ball indentation hardness H | 358N/30s | ISO 2039-1:1993 | 150N/mm2 |
Bending strength | 2mm/min | ISO 178:1993 | 100MPa |
HDT | 1.8MPa | ISO 75-2:1993 | 84°C |
efficient of thermal expansion | (23-80)°C | DIN 53 752 | 0.8-1.0K-1 |
Heat conduction | DIN 52 612 | 0.16W/mK | |
Vicat softening point | B50/oil | ISO 306:1994 | 93°C |
Flame retardance | >1.4mm | UL-Standard 94 | 94HBCla |
tem | Testing standards | Test Conditions | Units | PG-22 | PG-33 | PG-80 | PG-383 | |
Melt flow index | D-1238 | 200°C*5kg | g/10min. | 17.5 | 7.4 | 4.0 | 3.0 | |
Softening point | D-1525 | 1kg. | °C | 87.0 | 94.0 | 97.7 | 105.0 | |
Tensile strength | D-638 | Kg/cm² | 420 | 470 | 500 | 560 | ||
Tensile modulus | D-638 | 26460 | 26220 | 26720 | 28140 | |||
Bending strength | D-790 | Kg/cm² | 540 | 670 | 690 | 820 | ||
Flexural modulus | D-790 | Kg/cm² | 31000 | 31000 | 31000 | 33000 | ||
Heat distortion temperature | D-648 | °C | 75 | 79 | 81 | 86 | ||
Use | Mixed leveling | Injection level | Injection level | Board-level |