Item | Test Method | Unit | Value |
MFR (190°C,5.0kg) | ISO 1133 | g/10min | 0.4 |
MFR (190°C,2.16kg) | ISO 1133 | g/10min | 0.1 |
Density(polymer blends ) | ISO 1183 | g/cm3 | 0.959 |
Density(base resin) | ISO 1183 | g/cm3 | 0.949 |
|
|
|
|
Tensile Yield Strength | ISO/DIS6259 | MPa | 23 |
Izod impact strength (23°C) | ISO 79-LeU | KJ/m2 | No damage |
elongation at break | ISO/DIS6259 | % | >600 |
|
|
|
|
Flexural modulus | ASTMD790 | Kg/m2 | 9000 |
OTI (200°C,AI Pan) | ASTMD3895 | Min | >40 |
Brittleness temperature | ASTM D-746 | °C | <-70 |
ESCR (condition B,F20) | ASTMD1693 | Hr | >10000 |