1. Raw Material | ||||
HRC45 | HRC55 | HRC60 | HRC65 | |
YG10X | YG10.2 | K44 & K40 | Kennametal/Sandvik | |
Grain Size: 0.7um | Grain Size: 0.6um | Grain Size: 0.5um | Grain Size: 0.4um | |
Co: 10 % | Co: 10 % | Co: 12 % | Co: 12.5 % | |
Flexural strength: 3320N/mm2 | Flexural strength: 4000N/mm2 | Flexural strength: 4300N/mm2 | Flexural strength: 4300N/mm2 | |
Super Coating | ||||
AlTiN | TiAIN | TiSiN | Nano | |
Hardness(HV) | 3200 | 2800 | 3600 | 42(GPA) |
Thickness(UM) | 2.5-3 | 2.5-3 | 3 | 3 |
Oxidation Temp(°) | 900 | 800 | 1000 | 1200 |
Friction Coeffient | 0.3 | 0.3 | 0.45 | 0.4 |
Color | Black | Violet | Copper | Blue |