PVC Resin (Polyvinyl Chloride Resin) Used For Transparent Sheets→PVC S700 is mainly used to produce transparent sheets, which can be rolled into hard and semi hard sheets of the packaging, plates, floor materials, lining hard films (sugar paper, cigarette packaging film), etc. It can be extruded into hard and semi hard sheets for packaging, plates, profiled materials, and can be molded into joints, valves, electrical parts, auto parts and containers, etcPVC S800 is mainly used to produce transparent sheets, which can be rolled into hard and semi hard sheets of the packaging, cabinets, floor plates, and used for lining hard films, plates, records, profiles, joints, valves, electrical parts, auto parts, toys, bottles, containers, etc.PVC Resin Used For Soft Film→PVC S1000 can be used to produce soft film, sheet, artificial leather, pipe, profile, corrugated pipe, cable protection pipe, packaging film, sole and various soft sundriesPVC S1300 can be used for film, sheet, artificial leather, eath and various soft profiles.
PVC Resin Used For Injection Moulding→PVC H58 is used for Injection Moulding (Fitting), Blowing Moulding (Bottle);PVC H61 is used for Injection Moulding (Pipe Fitting), Hollow-vacuum Forming (Bottle Blowing), Rigid Film, Shrinkable Film;PVC Resin Used For High Impact Flexible Products→PVC H73 is used for High Impact Flexible Products (PVC Leather, Film, Furniture, Shoes), High Impact Sheet, High Voltage Insulation.Other→PVC Resin can be used for film, sheet, artificial leather, eath and various soft profiles.
| Item | Average temperature of polymerization | Viscosity /td> | K value | Polymerization Degree |
| SG1 | 48.2 | 154~144 | 77~75 | 1800~1650 |
| SG2 | 50.5 | 143-136 | 74-73 | 1650-1500 |
| SG3 | 53 | 135-127 | 72-71 | 1500~1350 |
| SG4 | 56.5 | 126-119 | 70-69 | 1250-1150 |
| SG5 | 58 | 118~107 | 68-66 | 1100-1000 |
| SG6 | 61.8 | 106-96 | 64-63 | 950-850 |
| SG7 | 65.5 | 95-87 | 62~60 | 850-750 |
| SG8 | 68.5 | 86-73 | 59-55 | 750-650 |
| CHEMICAL | HS-700 | HS-800 | HS-1000R | HS-1300 |
| Correspond GB Grade | SG-8 | SG-7 | SG-5 | SG-3 |
| 650-740 | 750-850 | 980-1100 | 1250-1350 | |
| K value | 55-59 | 60-62 | 66-68 | 71-72 |
| Viscosity /td> | 73-86 | 87-95 | 107-118 | 127-135 |
| Moisture,% | ≤0.50 | ≤0.50 | ≤0.50 | ≤0.50 |
| Apparent density, g/ml | 0.48±0.05 | 0.48±0.05 | 0.48±0.05 | 0.44±0.04 |
| Content of residue vinyl chloride, ppm | ≤1 | ≤1 | ≤1 | ≤1 |
| Grade(Test Method) | H-58 | H-61 | H-66 | H-73 |
| K-value(ISO 1628-2) | 57-59 | 60-62 | 65-67 | 72-74 |
| Degree of Polymerization | 700±50 | 800±50 | 1000±50 | 1350±50 |
| Bulk Density(g/cc)(ISO 60) | 0.57±0.04 | 0.57±0.04 | 0.54±0.04 | 0.51±0.04 |
| Particle Size(45 mesh pass %)(Honeywell SRA-150) | ≧99 | ≧99 | ≧99 | ≧99 |
| Volatiles(%)(ISO 1269) | ≦0.3 | ≦0.3 | ≦0.3 | ≦0.3 |
| Residual VCM(ppm)(ISO 6401) | <1 | <1 | <1 | <1 |
| Grade(Test Method) | S700 | S800 | S1000 | S1300 |
| Appearance | White Powder | |||
| Average Degree of Polymerization | 650~750 | 750~850 | 970~1070 | 1250~1350 |
| Apparent density,g/ml | 0.54~0.62 | 0.53~0.61 | 0.50~0.58 | 0.45~0.52 |
| Vilatile matter(including water content) | ≦0.20% | ≦0.20% | ≦0.20% | ≦0.20% |
| Absorption of 100g plasticizer,g | ≧14 | ≧16 | ≧20 | ≧27 |
| Residual vinyl chloride monomer content, ug/g | ≦3.0 | ≦3.0 | ≦3.0 | ≦2.0 |
| Reduce onSieve, 250μm Sieve mesh≤Sieve | ≦2.0% | ≦2.0% | ≦2.0% | ≦2.0% |
| Reduce onSieve, 63μm Sieve mesh≥Sieve | ≧95% | ≧95% | ≧97% | ≧95% |
| of Fish Eyes/400cm2 | ≦16 | ≦16 | ≦12 | ≦10 |
| of Impurity particles | ≦16 | ≦16 | ≦16 | ≦16 |
| Whiteness Degree(160(160°C,10min) | ≧75% | ≧75% | ≧78 | ≧78 |