Adhesive/glue/binders

This product is a dispersible liquid of the polydimethylsiloxane and resin among the methylbenzene, which is highly viscous and has good adhesion. It is a kind of goods with low smoke, non-idue, good stability, high temperature resistant, that can be used under 260℃ temperature. It also has the characteristics of exnt weather resistance, moisture resistance and electrical insulation.

Design application

●It is used for the production of high temperature tapes such as PET and PI.

●It is used for the production of electrical insulation, shading and sheet metal tape.

●It is used alone as a variety of adhesive, fixed or supported adhesives.

Basic technical data

●Appearance: colorless or light yellow semi transparent liquid, no mechanical impurities

●Diluting agent: methylbenzene/

●Viscosity（25℃mm2.S-1）：no less than 20000cs

●Solid content （150℃，2h，%）： 60±2

●Density (25℃): 0.98-1.01

Instruction for use

●Due to different factors such as substrate, coating equipment, curing period and required characteristics, the addition of curing agent ( peroxide can be used ,such as BPO or DPP, recommend with BPO) is 1-3% of the amount of glue. In order to ensure the best mixture of the curing agent and the adhesive, the curing agent needs to be completely dissolved in the solvent and then added to the glue solution and mixed well. At the same time, the dilution liquid should be filtered once with more than 180 mesh filter screen before coating on the machine, to prevent color paste or other impurity particles.

●The curing agent can be used to accelerate the curing speed or allow the curing at low temperature, and it also can improve the cohesion strength of the adhesive and improve the adhesion property of the adhesive. The mixed peroxide dispersion liquid should be used up within 1-2 days. That is because peroxide will lose its activity quickly in the solvents. The sufficient dispersion of adhesive and peroxide in the mixing process is the necessary condition to ensure the consistency of the finished product.

●SH - 916 adhesive can be directly coated with traditional tape coating equipment. The adhesive can be further diluted with the compatible solvent such as methylbenzene, dimetheylbenzene before coating. The advisable working liquid concentration is 35%. The concrete concentration is according to your respective equipment and experience. When using the solvents, please ensure that it is good ventilated and comply with safety precautions and regulations of solvent suppliers.

●In some applications, because of the lack of combination degree of the adhesive and backing material, it may be necessary to coat the prime coating before coating the adhesive. The primer coating must be cured before using, and the curing conditions depend on the equipment's performance, the type of base material and the formula used.

●Surface curing cycle: 60 ~ 90 ℃ * 1 min Eliminate the solvent to ensure that there is no solvent in the glue when it enters the solidification zone; 140 ~ 170 ℃ * 2 min, through the thermal curing to further improve the adhesive force, cohesive strength and initial adhesion. But the exact conditions required for full vulcanization depend on the length, temperature and efficiency of the furnace, the type of curing agent and the type of substrate used. It must be tested on the device to determine the condition.

●If the equipment and substrate allow higher curing temperature, the curing time can be shortened. Compared to low temperature curing, the high curing temperature can increase the cohesive strength of the adhesive in a shorter time.

Packaging, storage and transportation

Be packed in clean, dry 200kg steel drums and sealed. In the storage and transportation it must be closed in a cool ventilated and dry environment, avoid rain and sun exposure and avoid ng with acid, alkali or alkaounds and heavy metals. The storage period is 12 months. Exceeding the time it can be retested according to the rules again to check if it is qualified. Stored and transported as flammable goods.