| Commerical Grade Name | Hiperco 50A |
| Specifications | ASTM A801-14 Alloy 1 |
| Surface Finish | Ground Surface |
| Feature | High magnetic sturation alloy |
| Curie Point | 400℃ |
| Lead-Time | 4 week (Custom-Made Order)/4days (stocks) |
| Ceritificate | ISO9001:2015 |
| Process | Forging |
| Hiperco 50A | Full Magnetic Datasheet |
The alloy is melted using Vacuum Induction Melting (VIM) techniques.
| Commerical Trade Name | Hiperco 50A |
| Material | Iron-Cobalt Alloy |
| Specifications | ASTM A801-14 Alloy 1 |
| Surface Finish | Ground Surface |
| TOL.Diameter | +/-0.076mm |
| TOL.Length | +0.5mm |
| Melting Process | Vim Melting Techniques |
| Application | Turned components for actuators |
| Place of origin | Xi'an ,China |
Product Datasheet
Chemical Composition,%
C Max | Mn Max | Si Max | P Max | S Max | Cr Max | Ni Max | Co | V | Fe |
| 0.025 | 0.15 | 0.15 | 0.015 | 0.01 | 0.15 | 0.25 | 47.5-49.5 | 1.75-2.10 | Bal. |
sical Properties
| Density,g/cm3 | 8.12 |
| Resistivity | 0.40 |
| Curie Point | 940 |
| Melting Point C | 1427 |
| Elastic Modulus , Gpa | 207 |
| Hardness, Rockwell B | 20 |
| Thermal conductivity,W/(m·K) | 29 |
| Elongation , great than A | 7% |
| Satutation magnetostriction,10-6 | 60 |
DC magnetic properties Standard Min ValuesAfter Magnetic Final Annealing | |||||||
Material | Hc Max A/m | B at 400 A/m T | B at 800 A/m T | B at 1600 A/m T | B at 2500 A/m T | B at 4000 A/m T | B at 8000 A/m T |
Solid Material | 140 | 1.60 | 1.70 | 1.90 | 2.05 | 2.15 | 2.20 |
Strip Material | 110 | 1.70 | 2.00 | 2.10 | 2.15 | 2.20 | 2.25 |
Notes: Hc = coercive field strength, B = induction 1) annealed for optimum magnetic properties 2) annealed for optimum mechanical properties | |||||||
Typical Values of DC magnetic properties of solid materialAfter magnetic final annealing (solid material DIA.100mm) Typical Values | |||||||
Heat treatment temperature, °C | Hc A/m | µmax | B at 400 A/m T | B at 1600 A/m T | B at 2500 A/m T | B at 4000 A/m T | B at 8000 A/m T |
1150±5 ℃ | 98.47 | 7000 | 2.049 | 2.116 | 2.238 | 2.329 | 2.371 |
Test method: Machining the rod into 40mm OD and 32mm ID and final annealing. Then carried out of ring shape with winding of copper he material DC magnetic property by magentic tester. | |||||||
B-H Loop for Hiperco 50A
Magnetic field measured at B8000(A/m),Coercive field strength ,Hc=98.47(A/m) .Solid Material 100.0mm
Magnetization curve for Hiperco 50A
Magnetic field measured at B8000(A/m) ,induction (B)=2.371T, Solid Material 100mm
Application Examples:
Stamped lamination assemblies for motors and generators & Turned components for actuators
Notes: We are offering the heat-treatment processing techniques and Recommendation !
Further Process (Heat Treatment )
A final heat treatment ("magnetic final annealing") is mandatory for achieving the magnetic and mechanical properties. The necessary growth of the grains in the material, and hence the accompanying improvement in the characteristic magnetic values, only occurs during the final annealing.
Chemical composition,sical and Mechanical properties will be engineered according to specific customer requirements.Therefore chemical composition,sical and mechanical properties might be different to values listed in this document.Information about product characteristics or applicability of materials are shown only for informative purposes
Custom-made sample order support for Prototyping project. Meanwhile regular size are available in stock,The weight base on mill random length. MOQ 1PC
30% T/T in advance ,balance before shippment.
Mr. Paul (Designation :Foreign Trade Manager)
Signup today to claim your Discount. Get Started before it's too late!