Application
Silicon Carbide added to the furnace turn into the Si and C for casting iron, One is to improve the carbon content, and the second is to strengthen the reducibility of iron liquid. Greatly reduce the adverse effect of corrosion the furnace. Prevent carbide separate out, Increasing the amount ferrite, The cast iron compact structure, Significantly improve the processing performance and cutting face is bright and clean. Increase the nodular case iron grate ball per unit area. Improve sroidizing rate. For reducing nonmetallic inclusion and slag, eliminate shrinkage, eliminate subcutaneous blowhole also has a good effcet.
Standard
Grade Chemical Compositions (%)
SiC FC Fe2O3
â¥(Min) â¤(Max)
SiC-98 98.0 0.3 0.8
SiC-97 97.0 0.3 1.2
SiC-95 95.0 0.6 1.2
SiC-90 90.0 1.5 1.2
SiC-88 88.0 3.0 2.5
Size: 0-1mm; 0-3mm; 0-10mm; 1-10mm; etc
Packing: in 25kg bag or in 1mt big bag. etc
The specification, packaging and granular size can be produce according to customer demand.