PAT85 Plastic Material

This product, an Al2O3-SiO2 plastic material with very exnt plasticity and adhesion, good resistance to molten iron erosion, high post-curing strength and a capability of being put into use through simple baking after manual repair and construction, is applicable to the repair of the acid / neutral lining and molten iron ladle.Technical indicators

Maximum usage temperature

1,650℃

Volume density (g/cm3)

110℃×24h

2.4

Chemical components (%)

Al2O3

85

SiO2

4

ange (%)

1,000℃×3h

+ 0.2

Breaking strength in the cold state (MPa)

110℃×24h

9

1,000℃×3h

> 12.5

*All data listed above are typical.