Color | Black |
Description
1.Silicon nitride is a chemical compound of silicon and nitrogen. It is a hard ceramic having high strength over a broad temperature range, moderate thermal conductivity, low coefficient of thermal expansion, moderately high elastic modulus, and unusually high fracture toughness for a ceramic. This combination of properties leads to exnt thermal shock resistance, ability to withstand high structural loads to high temperature, and superior wear resistance.
Â
Classification:
Grinding Ball:the size is 1.5-40MM
Bearing Ball: the size is 0.4-60MM
sical Property and Index:
Types | Data |
Density | >3.2g/cm3 |
Flexural strength | 800-1200Mpa |
Compressive strength | >1500Mpa |
Thermal conductivity(W/mk) | 16-22 |
Porosity | 0 |
Thermal expansion coeff.(RT-1000ââÆ) | 3.2 |
Max temperature In air | 1200ââÆ |
Hardness(HRA) | >92 |
Â
Features:
1.Exnt corrosion resistance withstands attack from harsh chemicals and demanding environmental conditions.
2.Lightweight Silicon Nitride weighs 60% less than steel which reduces centrifugal force, skidding and wear under high speed and acceleration.
3.Superior Surface Finish, Ra 0.1 7-0.25 micro inches may extend L-10 life to as much as 10 times that of steel bearings.
4.High Temperature Hardness is twice that of steel. These all-ceramic balls retain their strength and hardness up to 1800 degrees F.
5.Silicon Nitride is further characterized by its low density of 3.2 g/cc, high flexural strength of 1.0 GPa, and fracture toughness of 6 MPa/M2.