100 Ton of EVA 2518 Resin properties: sical properties Typical Value1 Unit Test Method Melt Index (190°C 2.16 kg) 2.5 g 10 min ASTM D1238 Vinyl Acetate Content 18.2 wt% IPC Method Density 0.935 g cm3 IPC Method Vicat Softening Point 64 °C ASTM D1525 Melting Point 87 °C IPC Method Tensile Strength at Yield 5.2 MPa ASTM D6 Show More...
100 Ton of EVA 2518 Resin properties: sical properties Typical Value1 Unit Test Method Melt Index (190°C 2.16 kg) 2.5 g 10 min ASTM D1238 Vinyl Acetate Content 18.2 wt% IPC Method Density 0.935 g cm3 IPC Method Vicat Softening Point 64 °C ASTM D1525 Melting Point 87 °C IPC Method Tensile Strength at Yield 5.2 MPa ASTM D638 Tensile Strength at Break 14.7 MPa ASTM D638 Elongation at Yield 260 % ASTM D638 Elongation at Break >800 % ASTM D638 Flexural Modulus 60 MPa ASTM D790 Hardness Shore A 90 ASTM D2240 Hardness Shore D 38 ASTM D2240