Quick Details
- Commerical Grade Name:Hiperco 50A
- Specifications:ASTM A801-14 Alloy 1
- Surface Finish:Ground Surface
- Feature:high magnetic sturation alloy
- Curie Point:400℃
- Lead-Time:4 week (Custom-Made Order)/4days (stocks)
- Ceritificate:ISO9001:2015
- Process:Forging
- Hiperco 50A:Full Magnetic Datasheet
- Processing Time:4 weeks
- Port:xi'an
- Supply Ability: 2400 Kilograms Per Week
- Type:soft magnetic alloy
- Size:Dia.20 to 180mm
- Shape:Rod
- Raw Material:Iron -Cobalt
- Place of Origin:shaanxi,xi'an
- Model Number:Co50V2
- Application:rotor and stator laminations in motors and generators for aircraft power generation.
- Brand Name:XAGY
- Brand Name:XAGY
Hiperco 50A exhibit the highest magnetic saturation (2.4 T) of all soft-magnetic alloys. In addition, they exhibit low values of coercive force, meaning demagnetisation can be easily achieved. high DC maximum permeability and low AC core loss .
The alloy is melted using Vacuum Induction Melting (VIM) techniques.
Commerical Trade Name
Hiperco 50A
Material
Iron-Cobalt Alloy
Specifications
ASTM A801-14 Alloy 1
Surface Finish
Ground Surface
TOL.Diameter
+/-0.076mm
TOL.Length
+0.5mm
Melting Process
Vim Melting Techniques
Application
Turned components for actuators
Place of origin
Xi'an ,China
Product Datasheet
Chemical Composition,%
C
Max
Mn
Max
Si
Max
P
Max
S
Max
Cr
Max
Ni
Max
Co
V
Fe
0.025
0.15
0.15
0.015
0.01
0.15
0.25
47.5-49.5
1.75-2.10
Bal.
Physical Properties
Density,g/cm3
8.12
Resistivity
0.40
Curie Point
940
Melting Point C
1427
Elastic Modulus , Gpa
207
Hardness, Rockwell B
20
Thermal conductivity,W/(m·K)
29
Elongation , great than
A
7%
Satutation magnetostriction,10-6
60
DC
magnetic properties
Standard Min Values
After Magnetic Final Annealing
Material
Hc
Max
A/m
B at
400
A/m
T
B at
800
A/m
T
B at
1600
A/m
T
B at
2500
A/m
T
B at
4000
A/m
T
B at
8000
A/m
T
Solid Material
140
1.60
1.70
1.90
2.05
2.15
2.20
Strip Material
110
1.70
2.00
2.10
2.15
2.20
2.25
Notes:
Hc = coercive field strength, B = induction
1) annealed for optimum magnetic properties
2) annealed for optimum mechanical properties
Typical Values of DC magnetic properties of solid material
After magnetic final annealing (solid material DIA.100mm)
Typical Values
Heat treatment temperature, °C
Hc
A/m
µmax
B at
400
A/m
T
B at
1600
A/m
T
B at
2500
A/m
T
B at
4000
A/m
T
B at
8000
A/m
T
1150±5 ℃
98.47
7000
2.049
2.116
2.238
2.329
2.371
Test
method:
Machining the rod into 40mm OD and 32mm ID and final annealing. Then carried out of ring shape with winding of copper wire to test the material DC magnetic property by
magentic tester.
B-H Loop for Hiperco
50A
Magnetic field measured at B8000(A/m),Coercive field strength
,Hc=98.47(A/m) .Solid Material 100.0mm
Magnetization curve for Hiperco
50A
Magnetic field measured at B8000(A/m) ,induction (B)=2.371T, Solid Material 100mm
Application Examples:
Stamped lamination assemblies for motors and
generators & Turned
components for actuators
Notes:
We are offering the heat-treatment processing techniques and Recommendation !
Further
Process (Heat Treatment )
A final heat treatment ("magnetic final annealing") is
mandatory for achieving the magnetic and mechanical properties. The necessary growth of the grains in the material, and hence the accompanying improvement in the characteristic magnetic
values, only occurs during the final annealing.
Important Notice
1. Notice
Chemical composition,Physical and Mechanical properties will be engineered according to specific customer
requirements.Therefore chemical composition,physical and mechanical properties might be different to values listed in this document.
Information about product characteristics or applicability of materials are shown only for informative purposes
2. Sample Policy
Custom-made
sample order support for Prototyping project. Meanwhile regular size are available in stock,The weight base on mill random length. MOQ 1PC
3. Payment Terms
30% T/T in advance ,balance before shippment.
4. Who you talking to
Mr. Paul (Designation :Foreign Trade Manager)