Quick Details
- Commercial Grade Name:Hiperco 27
- Material:Iron-Cobalt Alloy
- Specifications:ASTM A801 Alloy Type 2
- Melting Process:Vim Melting Techniques
- Certificate:ISO9001:2015
- Surface Finish:Ground Surface
- Length Type:Mill Random Length or Per Requires
- Tol. Dia. (in mm):+/-0.0076
- Tol. L (in mm):+0.5/-0.0
- Heart Treatment Temperature:910 +/-10 C H2 Protection for 5 Hours
- Incoterms:EXW,Fob,CIF,DDU,DDP
- Delivery Tolerance:+/-10 %
- Production Period:4 Weeks (Custom-Made Orders)
- Features:High Magnetic Sturation Alloy
- Transport Package:Ex. Gross Weight Under 20kg = Carton Box / Gross Weight Over 20kg = Plywood Box Or As Per Request
- Additional Comments:Heat-Treatment Processing Techniques Recommend
- Processing Time:4 week
- Port:ShangHai
- Supply Ability: 1200 Kilograms Per Month
- Brand Name:Xagy
- Model Number:Co27Fe
- Size:Dia.20 to 500mm
- Type:Round Rod
- Shape:Rod & Disc
- Raw Material:CoFe
- Place of Origin:Shaanxi,xi'an
- Application:magnetic pole caps, and laminations for aircraft motors and generators
- Brand Name:XAGY
Product Description
Hiperco27
is a new kind of soft magnetic alloy and also called FeCo27. while its permeability and the coercive force slightly smaller than hiperco50, but the mechanical toughness and ductility is better,
can be competent for machining, the saturated magnetic induction intensity and Curie temperature are fairly to HiperCo 50 .
Commercial Grade Name
Hiperco 27
Material
Iron-Cobalt Alloy
Specifications
ASTM A801-14 Alloy 2
Melting Process
Ground Surface
Melting Process
Vim Melting Techniques
TOL. .Diameter
+0.3/-0.00mm
Forms of supply
Rod
Strip
Plate
Dia.20 to 380mm,
T0.1 to 1.51mm
T1.51 to 40.0mm
Surface Finish: Ground Surface
Surface Finish: Cold-Finish
Surface Finish: Hot-Rolled
Chemical Compostition,%
C,Max
Mn,Max
Si,Max
P,Max
S,Max
Cr,Max
Co
V,Max
Ni,Max
Fe
0.025
0.35
0.35
0.015
0.015
0.75
26.5-28.5
0.35
0.75
Ba.
Notes:
The shape and dimensions of the alloys are in compliance with ASTM A801 UNS K92600
Physical Property
Density, G/m3
7.95
Electrical Resistivity
0.19
Curie Temperature, C
925
satutation Magnetostriction
36
Modulus of elasticity,Gpa
166
Saturation Induction,T
2.36
Thermal Expansion,(20 to 100 C)
9.8
DC Magnetic Properties (Magnetic induction at different magnetic field B, Great Than (T) )
Material
B4000,A/m
T
B8000,A/m
T
B12000,A/m
T
B16000,A/m
T
Coercivity
Hc(A/m),Max
Strip Material
1.87
2.03
2.12
2.17
140
Soild Material
1.10
1.75
1.95
2.10
240
Hc = Coercive field strength,Maximum Value in the table,Typical Value for Soild Material,Hc less Than 190(A/m)
B = Induction (minimum value in the table,Typical Value for strip material,T Great than 2.15(A/m)
Annealed for optimum magnetic properties
B-H Loop
Magnetic field measured at B9992(A/m)=2.173T , Soild Material Dia.100.0mm
Magnetization curve
Magnetic
field Measured at B9992(A/m),Coercive field strength ,Hc=169.5(A/m) .Soild Material 100.0mm
Further-Process (Heat Treatment)
Use a non-oxidizing ,non-carburizing atmosphere such as dry hydrogen,argon,or equivalent ,or a Vacuum. Appropriate safety precaution must be taken when working with highly
flammable atmospheres.
Important Notice
Chemical composition,Physical and Magnetic properties will be engineered according to specific customer requirements.Therefore chemical
composition,physical and magnetic properties might be different to values listed in this document.
Information about product characteristics or applicability of materials are shown only for informative purposes.Sample policy
The soft magnetic Iron-Cobalt Alloy are available in many shapes and
dimensions,supplying semi-finished products in forms of Strip,plate & Rods.
The samples are big enough (typically about 200mm in length for strip or plate) to get an understanding of the material characteristics,
.meanwhile custom-made sample available.
If you still have questions
about the material , do not hesitate to contact Paul with any specific questions.