Quick Details
- Processing Time:25days
- Port:Shanghai
- Supply Ability: 260000 Tons Per Month
- Usage:shoe sole
- Purity:100%
- Place of Origin:China
- Other Names:Polyurethane resin
- Brand Name:Xuchuan
- CAS No.:9009-54-5
- Brand Name:Xuchuan
Production Description
Characteristic: Good handle,
hydrolysis resistance, high strength and cohesive force, good abrasion resistance and skid resistance
Application: Double density sole system for
common safety shoes and one-step forming casual shoes, outsole
Typical properties of PU matrix
Name of product
Appearance
Viscosity (mPa·s)
Density (g·cm-³)
Package (kg)
A-6002
Liquid
1000-1400
1.01-1.02
18
B-8280
Yellowish transparent liquid or waxy
600-1000
1.08-1.2
20
Materials preheat
A-6002: preheated at 50-60 ℃ for 6-8 hours
B-8280: preheated at 50-60 ℃ for 8-12 hours
Typical processing parameters & Reaction parameter
Items
A/B Materials Temperatures(℃)
Mix ratio A+C/B
(By weight)
Cream time
(s)
End of Rise Time
(s)
Parameter
40-45/40-45
sole
mid-sole
sole
mid-sole
40-50
100/72-74
100/78-80
6-8
6-7
Items
Free Rise Foam Density
(g/cm³)
Mold Temperature
(℃)
Demold Time
(min)
parameter
sole
mid-sole
45-55
5-7
0.50-1.0
0.23-0.27
The adding content of C-2 should be 300g±10g/18kg
The adding content of water and hardener should be changed according to the reality
Sole: H2O 0-20g/18kg Hardener 0-400g/18kg
Mid-sole: H2O 50-60g/18kg Hardener 0-600g/18kg
Physical properties
Items
Molded Density
(g/cm³)
Hardness
(Shore A)
Tensile strength
(Mpa)
Elongation
(%)
Physical
properties
sole
mid-sole
sole
mid-sole
sole
mid-sole
sole
mid-sole
0.8-1.1
0.45-0.55
55-70
38-50
7.5-11.0
3.9-7.9
550-750
520-690
Items
Tear strength
(kN/m)
Flexing resistance
DIN abrasion
(mm³)
Peel strength between sole and mid-sole
(kN/m)
Physical properties
sole
mid-sole
100000 times no crack
sole
mid-sole
≥3.5
27-40
18-25
60-100
----
Demold time may be prolonged with the increse of sole thickness
These physical data are acquired by testing a sample of 6mm thick
Data listed above are just for reference.The data are subjected to practical production.If other requests for physical properties,please contact us.