Quick Details
- Processing Time:-
- Port:-
- Supply Ability: -
- Brand Name:-
MATERIAL CATEGORY: High temperature martensitic high content chromium round bar
and forge piece
MATERIAL SPECIFICATIONS: ASTM
A565
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.20 ~ 0.25
Si (%): ≤ 0.50
Mn (%): 0.50 ~ 1.00
P (%)≤: 0.025
S (%)≤: 0.015
Cr (%): 11.0 ~ 13.5
Ni (%): 0.50 ~ 1.00
Mo (%): 0.90 ~ 1.25
W (%): 0.90 ~
1.25
V (%): 0.20 ~
0.30
Others (%): Cu ≤
0.50
MECHANICAL
PROPERTIES / HEAT TREATMENT OR Q/T
Condition of heat
treatment: Annealed
Tensile strength,
σb ≥/MPa: -
Yield strength, σ0.2
≥/MPa:-
Elongation, δ
≥(%): -
Reduction of area, ф ≥(%): -
Hardness | HRS:
≤248
Condition of heat treatment: T, middle
tempered
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2
≥/MPa:-
Elongation, δ ≥(%): -
Reduction of area, ф ≥(%): -
Hardness | HRS:
≤285
Condition of heat
treatment: HT 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2H, tempered
Tensile strength, σb
≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ
≥(%): 13.0
Reduction of area, ф ≥(%): 30.0
Hardness | HRS: 302 ~ 352
Condition of heat treatment: H 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X
2H, tempered
Tensile strength, σb ≥/MPa: 825
Yield strength, σ0.2 ≥/MPa:
585
Elongation, δ ≥(%): 17.0
Reduction of area, ф ≥(%): 35.0
Hardness | HRS: 241 ~
285