High Silica Fiberglass Filter Mesh for Molten Aluminum Steel Foundry Filtration
High Silica fiberglass filter mesh is weaved with high silica fiberglass yarn and coated with special refractory coating. It can effectively remove slag, refractory
particles and non-metallic inclusions from molten metals. After special treatment, high silica mesh filters are capable of withstanding pouring temperatures up to 1620℃.
High Silica fiberglass mesh is an ideal filter for in-mold filtration of gray, malleable, white, compacted graphite and ductile cast irons, as well as non-ferrous aluminum and copper-based metal
alloys and many types of small scale steel casting filtration. Besides the function of molten metal filtration, it also could be used for riser knock-off or de-gating knock-off. Investment
casters have also placed the preformed cup shape filters in the wax mold gating system to filter metal at pattern entry. It is developed as a low cost but with rather filtration
efficiency alternative to ceramic filters.
Product Features
• Low cost and easy to use
• Improves fluidity and metal distribution
• Removes micron sized inclusions and impurities
• Can be used with existing pattern equipment
• Eliminates inclusions created by ceramic chips
Product Parameters
SiO2 content
≥96%
Softening Point
1700℃
Working Temperature
≤1620℃
Sustaining Working Time
5 minutes
Tensile Strength
16kg/4 ends
Color
Dark brown, black
Mesh Size
0.8mm/1.0mm/1.5mm/2.0mm/2.5mm
Density
300-600 g/cm2
Thermal Shock Resistance
≥2times/1100ºC‐Room
temperature
Specification:
Item
Density
Mesh size
Porosity
SiO2
Thickness
HSWM-15
580g/m2
1.5x1.5mm
0.19
≥96%
0.98mm
HSWM-20
460g/m2
2.0x2.0mm
0.24
≥96%
0.98mm
HSWM-25
350g/m2
2.5x2.5mm
0.33
≥96%
0.98mm
Note: other specifications made as requests.
Application:
- Cut pieces for in mold filtration like sand casting, gravity casting, etc.
- Cut pieces for riser sleeves, bottom or across ports in walls
- Cut pieces to provide a weakened plane for riser knock-off
- Cup shapes for investment casting