Quick Details
- C:90-97
- S:0.02-0.5
- Processing Time:7-15
- Port:Tianjin port or other ports
- Supply Ability: 3000 Tons Per Month
- Brand Name:JY
I. Product Description:
本碳素添加剂采用添加剂天然石墨粉，经高温热处理，经机压成块，经研磨、筛分、加工成适合客户使用的优质添加剂碳素。该产品熔化快，吸收好，促进铸件中A型石墨的析出，有效提高产品性能。
2. the use of carbon enhancer:
1、Adjust the carbon content when dosing, according to the requirements of the carbon content of the molten steel (iron), the calculated carbon additive will be added to the bottom of the furnace
with the metal charge, the absorption rate of carbon up to 90%-95%, to be fully melted and absorbed by the carbon additive and then slagging. Note: The first furnace melting words to add
high-quality iron scrap or scrap steel in the bottom of the furnace first after the bottom of the iron, and then add the carbon enhancer to the bottom, the second furnace from production to take
the remaining 40-60 kg of iron in the last furnace, if the carbon enhancer to add a larger amount to join in batches to help the carbon better absorption. Add the bottom of the recommended use of
1-5mm or 1-8mm particle size.
2、After the steel (iron) water melting, the carbon of the molten iron is fine-tuned and can be added to the surface of the steel (iron) water, and the carbon is dissolved and absorbed through the
vortex stirring of the steel (iron) water or artificially stirred off during the electric furnace melting. This kind of recommended use 1-3mm particle size.
3、 the furnace input method.