Round bar steel in Nitronic 50HS and 17-4PH in condition H1150D Buyer and Importer
1) material Nitronic 50 HS (High Strength)/ EU Code 1.3964/ XM-19HS/ UNS S20910
Nitronic 50 HS = 930 RM Tensile strength, = 800 Rp 0,2% Yield strength, = 325 HB Hardness
always necessary with inspection certificate 3.1 and NACE MR 0175/ 2003/ ISO 15156
requirements:
AK Steel 007 1 XM-19HS
ISO 148-3:2016 Impact test (-196°C, 27J)
ASME SA479 2015
ASTM A182 2016 chemical analysis
ASTM A262 2015
ASTM A370 2017
ASTM A479 2017 S20910 H
Diameter:
D=12,7mm (60m in random length)
D=22,22mm (24m in random length)
D=31,75mm (48m in random length)
D=41mm (18m in random length)
D=45mm (36m in random length)
D=50,8mm (36m in random length)
D=60mm (12m in random length)
D=70mm (12m in random length)
D=90mm (12m in random length)
D=101,6mm (18m in random length)
D=120mm (12m in random length)
D=145mm (2965mm cut length)
D=160mm (3360mm cut length)
2) material 17-4 PH in condition H1150D double certified/ EU Code 1.4542/ UNS 17400 PH
17-4 PH in condition H1150 D with double heating treatment:
620°C/ 4h/ air
+ 620°C/ 4h/ air
= 900 RM Tensile strength, = 725 Rp 0,2% Yield strength, = 255 min. - 308 max. HB Hardness
always necessary with inspection certificate 3.1 and NACE MR 0175/ 2003/ ISO 15156
requirements:
AK Steel 009 2014 1.4542/630 H1150D
AMS 5643 R S17400 chemical analysis
ISO 148-3:2016 Impact test (-196°C, 41 KV J)
ASME SA564 2017 S17400 H1150D
ASTM A370 2017
ASTM A564 2013 S17400 H1150D Solution treated-air cooled-aged H1150+H1150
EN 10088-3 2005 1.4542 (5) chemical analysis only
Diameter:
D=18mm (24m in random length)
D=22,25mm (24m in random length)
D=28,6mm (24m in random length)
D=32mm (48m in random length)
D=40mm (24m in random length)
D=45mm (48m in random length)
D=51mm (48m in random length)
D=60mm (24m in random length)
D=63,5mm (24m in random length)
D=70mm (24m in random length)
D=90mm (24m in random length)
D=95,5mm (24m in random length)
D=102mm (30m in random length)
D=120mm (18m in random length)
Incoterm: FOB
black surfacegth, = 325 HB Hardness
always necessary with inspection certificate 3.1 and NACE MR 0175/ 2003/ ISO 15156
requirements:
AK Steel 007 1 XM-19HS
ISO 148-3:2016 Impact test (-196°C, 27J)
ASME SA479 2015
ASTM A182 2016 chemical analysis
ASTM A262 2015
ASTM A370 2017
ASTM A479 2017 S20910 H
Diameter:
D=12,7mm (60m in random length)
D=22,22mm (24m in random length)
D=31,75mm (48m in random length)
D=41mm (18m in random length)
D=45mm (36m in random length)
D=50,8mm (36m in random length)
D=60mm (12m in random length)
D=70mm (12m in random length)
D=90mm (12m in random length)
D=101,6mm (18m in random length)
D=120mm (12m in random length)
D=145mm (2965mm cut length)
D=160mm (3360mm cut length)
2) material 17-4 PH in condition H1150D double certified/ EU Code 1.4542/ UNS 17400 PH
17-4 PH in condition H1150 D with double heating treatment:
620°C/ 4h/ air
+ 620°C/ 4h/ air
= 900 RM Tensile strength, = 725 Rp 0,2% Yield strength, = 255 min. - 308 max. HB Hardness
always necessary with inspection certificate 3.1 and NACE MR 0175/ 2003/ ISO 15156
requirements:
AK Steel 009 2014 1.4542/630 H1150D
AMS 5643 R S17400 chemical analysis
ISO 148-3:2016 Impact test (-196°C, 41 KV J)
ASME SA564 2017 S17400 H1150D
ASTM A370 2017
ASTM A564 2013 S17400 H1150D Solution treated-air cooled-aged H1150+H1150
EN 10088-3 2005 1.4542 (5) chemical analysis only
Diameter:
D=18mm (24m in random length)
D=22,25mm (24m in random length)
D=28,6mm (24m in random length)
D=32mm (48m in random length)
D=40mm (24m in random length)
D=45mm (48m in random length)
D=51mm (48m in random length)
D=60mm (24m in random length)
D=63,5mm (24m in random length)
D=70mm (24m in random length)
D=90mm (24m in random length)
D=95,5mm (24m in random length)
D=102mm (30m in random length)
D=120mm (18m in random length)
Incoterm: FOB
black surface
Show More
- Posted On:03 May, 2024
- Company Name:Show
- Contact Number:Show
- Purchaser:Daniel Esser
- Quantity Required16000 Kilogram
- Buying FrequencyQuarterly
- Destination Port RDM Rotterdam
- Time of Validity6 Months