REMI-CALCIUM SILICATE BOARD-HIGH DENSITY–
is as bestos free and high temperature insulation board , which possess higher density and also higher strength and prefect handling characteristic .
Properties:
-Lower Thermal Conductivity
-Higher Strength,
-Higher Application Temperature
-Resistance to Moisture
-Resistance to Chemical and
Corrosion
ApplicationParmenant Ladle, Tundish, Tropedo Car , Furnace and Alumina Industries .
Shaped Insulating Parts
| Calcium Silicate Board -Higher Density | |||
| Application Temperature | oC | 1000 | |
| Conbustion Proformance | A grade | ||
| Density(dired) | kg/m3 | 900±10% | |
| Thermal Conductivity | W/m.K | 0.13(at 200oC) | |
| Cold Crushing Strength | Mpa | 13 | |
| Modulus Rupature | Mpa | 6 | |
| Shrinkage at1000oC*3hr | % | 2max | |
| L.O.I | % | 9max | |
| value | 7~9 | ||
| Moisture | % | 6max | |
| Color | White | ||
| Odour | No any | ||
| Solubility | Insoluble in water and Organics | ||
| Asbestos Free and No r> | |||
| Size | mm | 300*114, 300*150*2400 | |
| Thickness | mm | 10-50 | |
| Tolerance | mm | Thickness±0.5, L&W±3 | |
REMI-CALCIUM SILICATE BOARD-general grade divided into 650oC (5CaO*6SiO2*5H2O) and 1050oC (6CaO*6SiO2*H20) . Based on the lower themal Conductivity , they are wildly applied in Insulation of Industiral Furnace and Pipe to dedrease the heating loss.
| Calcium Silicate Board 1050oC Grade | |||
| Items | Unit | HSC-170 | HCS-220 |
| Density | Kg/m3 | 170 （±10%） | 220 （ ±10%） |
| Cold Crushing Strength | MPa | 0.4 | 0.5 |
| Compressive Strength | MPa | 0.3 | 0.35 |
| Thermal Conductivity | W/m.K | 0.048(+0.00011t) | 0.05(+0.00011t) |
| Top Service Temp | °C | 1050 | 1050 |
| Shrinkage | % | 1.5(1000oC*3h) | 1.5(1000oC*3h) |
| Calcium Silicate Board 650oC Grade | ||||
| HCS-270 | LSC-170 | LSC-220 | LSC-270 | |
| 270 （±10%） | 170 （±10%） | 220 （±10%） | 240 （±10%） | |
| 0.6 | 0.4 | 0.5 | 0.5 | |
| 0.4 | 0.2 | 0.3 | 0.3 | |
| 0.056(+0.00011t) | 0.058 | 0.062 | 0.062 | |
| 1050 | 650℃ | 650℃ | 650℃ | |