| Aluminium Alloy | 6063,6060,6061,6063A |
| Temper | T4-T6 |
| Quality Standard | China National Standard GB/T 5237-2008 (advanced class) |
| Quality Certificate | ISO9001, ISO14001,OHSAS18001,DNV,QUALANOD, QUALICOAT |
| Use Purpose | Construcion,Industrial |
| Surface Treatment | Mill finish, Polished, Anodizing, Powder coating, Wood-grain painting |
| Color | Silver, Bronze, Champagne, Black,Golden,Titanium golden,wood-grain |
| Shape | Various shapes, parameters and colors can be customized |
| Thickness | Customized |
| Packing | Bundles packing,Carton Packing,Wooden Pallet Packing |
Aluminum extrusion is a technique used to transform aluminum alloy into objects with a definitive cross-sectional profile for a wide range of uses. The extrusion process makes the most of aluminum’s unique combination of sical characteristics. Its malleability allows it to be easily machined and cast, and yet aluminum is one third the density and stiffness of steel so the resulting products offer strength and stability, particularly when alloyed with other metals.
Today, aluminum extrusion is used for a wide range of purposes, including components of the International Space Station. These diverse applications are possible due to the advantageous attributes of aluminum, from its particular blend of strength and ductility to its conductivity, its non-magnetic properties and its ability to be recycled repeatedly without loss of integrity. All of these capabilities make aluminum extrusion a viable and adaptable solution for an growing of manufacturing needs.
Composition of Alloy| Aloy | Si | Mg | FE | CU | MN | ZN | CR | Ti | Impurity | Al | |
| Unit | Total | ||||||||||
| 6061(%) | 0.40-0.8 | 0.8-1.2 | <0.7 | 0.15-0.40 | <0.15 | <0.25 | 0.04-0.35 | <0.15 | <0.05 | <0.15 | Remainder |
| 6063(%) | 0.20-0.6 | 0.45-0.9 | <0.35 | <0.10 | <0.10 | <0.10 | <0.10 | <0.10 | <0.05 | <0.15 | Remainder |
| 6063A | 0.30-0.6 | 0.6-0.9 | 0.15-0.35 | <0.10 | <0.15 | <0.15 | <0.05 | <0.10 | <0.05 | <0.15 | Remainder |
Mechanical Properties of Sections under Room Temperature
| Alloy | Temper | Tensile strength test | Hardness test | |||||
| mm | Tensile strength RM/(N/mm²) | Non-proportional Stretching Stress Rp0.2/(N/mm²) | Streching rate A50mm | Pattern Thickness (mm) | HV | HW | ||
| 6061 | T4 | ALL | ≥180 | ≥110 | ≥16 | - | - | - |
| T6 | ALL | ≥265 | ≥245 | ≥8 | - | - | - | |
| 6063 | T5 | ALL | ≥160 | ≥110 | ≥8 | ≥0.8 | ≥58 | ≥8 |
| T6 | ALL | ≥205 | ≥180 | ≥8 | - | - | - | |
| 6063A | T5 | ≤10 | ≥200 | ≥160 | ≥5 | ≥0.8 | ≥65 | ≥10 |
| >10 | ≥190 | ≥150 | ≥5 | |||||
| T6 | ≤10 | ≥230 | ≥190 | ≥5 | - | |||
| >10 | ≥220 | ≥180 | ≥4 | |||||