Polypropylene Nylon Sheet

Properties Standard Unit Result

mechanical property

Density ASTM D792 g/cm3 1.13

Tensile strength ASTM D638 Mpa 74

ultimate elongation ASTM D638 % 5

bending strength ASTM 790 Mpa 90

bending modulus ASTM 790 Mpa 2200

hardness ASTM D2240 D 85

Impact strength ASTM D256 J/M 50

Thermal properties

Melting poing DSC ℃ 220

working Temp. ASTM D648 ℃ 70

Permanent Temp. - ℃ 85

Short-period Temp. - ℃ 160

Pyroconductivity DIN 52612-1 W/(K-M) 0.23

dilatation coefficient ASTM D696 10-5-1/K 8

electrical property

dielectric strength ASTM D150 KV-mm 25

dielectric loss coefficient ASTM D150 - 0.032

Volume resistance ASTM D257 Ω.cm 1014

surface resistance ASTM D257 Ω 1016

dielectric constant ASTM D149 - 4.2

Chemical properties

Water absorption 23℃ 60%RH % 1.28

Acid resistance 23℃ 60%RH -

Alkali resistance +

Resistance to acid and alkali water +

Chloric acid alkali resistance 0

Resistant to aromatic compounds +

The ketone resistance 23℃ 60%RH +

Water resistance 23℃ 60%RH +

Others properties

combustibility UL 94 HB

paste - +

Non-s EEC 90/128 FDA +

friction coefficient DIN 53375 0.36

uvioresistant - -

<spanVerdana",sans-serif; mso-bidi-font-family:SimSun;color:#222222;mso-font-kerning:18.0pt">Nylon Sheet

<spanArial",sans-serif; color:#222222;mso-font-kerning:0pt">Nylon was the first engineering resin and has been used in applications ranging from electronic, marine, and automotive industries to fibers used to make carpet. Nylon sheet has outstanding wear resistance and low frictional properties.

<spanArial",sans-serif; color:#222222;mso-font-kerning:0pt">Nylon has very good temperature, chemical, and impact properties. Parts machined or fabricated from nylon are light weight and corrosion resistant. Low friction, good abrasion resistance and the ability to operate without lubrication, qualify the nylons for such applications. Parts machined or fabricated from cast nylon are light weight and corrosion resistant. In addition, cast nylon's exnt load bearing capability, wear resistance and impact resistance make it ideal for demanding construction environments.

<spanArial",sans-serif; color:#222222;mso-font-kerning:0pt">Nylon sheet which has not been compounded with UV stabilizers are sensitive to ultraviolet light. These compounds should not be used for extended outdoor service. Carbonblack (<spanArial",sans-serif; color:#222222;mso-font-kerning:0pt">our black Nylon Sheet<spanArial",sans-serif;color:#222222;mso-font-kerning: 0pt">) is the most effective of the UV stabilizers. These additives also increase tensile strength and hardness and decrease ductility and toughness slightly.

Features<spanArial",sans-serif; color:#222222">

• Good abrasion and wear resistance
• Continuous use temperature of 220°F
• Very easy to fabricate
• Outstanding chemical resistance to alkalies and oxidizing agents
• High strength and stiffness at elevated temperatures
• Light weight (approx. 1/8 vs. bronze)
• Good impact strength at low temperature
• Low friction coeficient
• FDA & USDA (Natural)

<spanArial",sans-serif; color:#222222">Applications

• Bushings
• Bearings
• Rollers
• Manifolds
• Gears
• Sprockets
• Sheaves
• Insulators
• Wear components

<spanArial",sans-serif; color:#222222">Certifications

• ASTM
• FDA