fireproof 1260 stanard spun ceramic fiber heat insulation glass wool
Description
Common Fibre: With hard clay clinker as raw material, made from melting,blowing,spun by the resistance furnace.High purity Fibre: With high purity alumina and silica as raw material, made from melting,blowing,spun by the resistance furnace.Cerachem Fibre: With alumina,silica and zirconia as raw material, made from melting,blowing,spun by the resistance furnace.Cerachrome Fibre: With,silica and chromia as raw material, made from melting,blowing,spun by the resistance furnace.Spun Fibre: Contain lubricant ,low residue ball content,high fibre material content, and spun without processing turns to be long fibre, is the gap fillers of wall lining of high temperature kiln heating device and raw material for yarns Blowing Fibre: No lubricant,no processing,low residue ball content, is the gap fillers of high temperature kiln, and raw material for vacuum forming products,,Features
Exnt thermal stability, resist devitrification at high temperature.Low heat strong capacity, Low thermal conductivity Contain no binders or corrosive agentsResilient up to high temperaturesExnt sound absorberTypical Application
Raw material for the manufacturing of finished products such as boards, paper, shapes, yarns etcPacking expansion joints and material for temporary repair of insulationRaw material for Fiber spraying,castable and daub materialLoose insulating fill for complex spaces and areas where access is difficultDate sheet
Type | CT 1100 | CT 1260 | CT 1360 | CT 1430 | CT 1500 |
Classification Temperature(°C) | 1100 | 1260 | 1360 | 1430 | 1500 |
color | white | Pure white | Pure white | Pure white | Blue/green |
Fiber diameter(um) | blowing | 2-3 | 2-3 | 2-3 | 2-3 | 2-3 |
spun | 3-4.5 | 3-4.5 | 3-4.0 | 3-4.0 | 3-4.0 |
Chemical Composition(%) | Al2O3 | 42-44 | 45-46 | 52-55 | 39-40 | 43 |
Al2O3+SiO2 | 96 | 98 | 99 | 99 | 99 |
ZrO2 | - | - | - | 15-17 | - |
Cr2O3 | - | - | - | - | 2.5-3.0 |
Remark
The values given herein are typical average values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Therefore, the data contained herein should not be used for specification purposes.